Founded in 1978, Zhongde is a professional injection molding supplier focusing on OEM ODM customized services. Based on 40 years technology deposition, we have developed a one-stop solution from mold designing and rapid prototyping to mass production. Our manufacturing capabilities include plastic injection molding service, compression molding service, CNC machining service, metal stamping service, 3D printing service, custom molding service,etc.
Selective Laser Sintering SLS is an industrial 3D sintered laser printing process ideal for manufacturing end-use parts. In SLS, a laser selectively sinters polymer powder particles, fusing them together and building a part layer-by-layer. From prototyping to small-batch production, our 3d laser sintering printing facilities will allow you to produce highly accurate parts with quality and strength comparable to injection molding.Now the selective laser sintering cost is low.
SLS produces functional plastic parts with isotropic mechanical properties that can be used for detailed prototyping or end-use low-volume production.
Guideline of Fused Deposition Modeling
Size of Selective Sintering
Below table shows the size of Fused Deposition Modeling parts we usually make. If you need a larger size, we can also help you achieve it.
Standard capabilities Description
Maximum build size 300 x 300 x 300 mm 11.8” x 11.8” x 11.8”
Lead time 6 business days
Dimensional accuracy ± 0.3% with a lower limit of ± 0.3 mm ± 0.012”
Layer thickness 100 ?m
For expedited lead times or parts that exceed the maximum build size contact firstname.lastname@example.org.
Available Materials of Selective Laser Sintering
In addition to the general materials listed below, Zhongde can also modify the materials according to the special needs of customers. Our professional engineers will adjust the raw material formula to meet the unique conditions of use.
Nylon 12 PA 12 SLS nylon is a robust thermoplastic with all-around excellent physical properties, ideal for functional prototypes and end-use applications.
Glass-filled Nylon PA 12 GF Glass-filled SLS nylon is reinforced with glass beads creating parts with higher stiffness and thermal stability than standard nylon.
TPU / TPE / TPA Thermoplastic elastomers combine high elasticity and strength with good chemical resistance, making them ideal for functional, flexible parts.
These materials are available by contacting email@example.com.
Design Guidelines of Selective Laser Sintering
The following table summarizes the recommended and technically feasible values for the most common features encountered in 3D printed parts.
Feature Recommended size
Unsupported walls 1.0 mm 0.040''
Supported walls 0.7 mm 0.030''
Minimum detail size 0.25 mm 0.010''
Minimum hole size 1.0 mm 0.040''
Moving parts 0.5 mm 0.020'' between moving surfaces
Assembly clearance 0.4 mm 0.016'' between mating surfaces
Maximum wall thickness 20 mm 0.8''. Thicker parts must be hollowed with and at least two escape holes for powder removal with a min. diameter of 8 mm 0.3''.
Available Surface Finishes of Selective Laser Sintering
Additional post processes can be applied to improve the appearance or mechanical properties of parts produced with SLS.
As printed As printed SLS parts are typically white or stone grey in color with a smooth surface and a powder texture and without visible layers.
Dyed SLS parts can be dyed by immersing in a warm color bath to a variety of colors. The color penetration reaches an approximate depth of 0.5 mm and covers all surfaces.
Tumble smoothing The parts are placed in a tumbler that contains small ceramic chips, gradually eroding its surface down to a polished injection molding-like finish.
Bead blasting Bead blasting shot pinning adds a uniform matte or satin surface finish on a 3D printed part.
Spray painting SLS parts can be spray painted white, black or to a specified RAL or Pantone color.
Water tightening SLS parts are vacuum impregnated with resin, sealing all internal porosity and ensuring water tightness.
Metal plating Electroplating nickel, copper or gold is an ideal solution for parts that require a metallic appearance, without the high costs associated with metal 3D printing.